Water-borne firm coating compositions and processes therefor

ABSTRACT

Water reducible, dispersible coating composition comprising: organic vehicle containing wax compounds of low oil content, neopentyl ester, carboxylic acid, amine, alcoholic coupling solvent, water. Vehicle is preferably amine salt of organic wax of low oil content, long-chain carboxylic acid and neopentyl ester, e.g. C30 acid and pentaerythritol.

CROSS REFERENCES TO RELATED APPLICATIONS

The present application discloses compositions and techniques related to those of U.S. patent application Ser. No. 374,467, filed May 3, 1982, and also to U.S. patent application Ser. No. 382,853, filed May 24, 1982, also to U.S. patent application Ser. No. 374,466, filed May 3, 1982.

BACKGROUND OF THE INVENTION

(1) Field of the Invention:

The present invention relates particularly to organic coating compositions and methods for their use generally classified in Class 106, particularly in Subclasses 14.11, 14.13, 14.15, 14.16, 14.34, 14.35, 14.37, 14.38, 270, 271 and 272.

(2) Description of the Prior Art:

U.S. Pat. No. 3,539,367 to Yaroshevich, et al discloses a wax emulsion containing a salt of an organic acid and an amine. U.S. Pat. No. 3,660,128 to Sheldahl teaches an alkanolamine and an aliphatic carboxylic acid in the preparation of a semi-solid wax-in-water emulsion. U.S. Pat. No. 2,349,326 to Wilson teaches a combination of morpholine and a fatty acid to emulsify waxy materials in water for paste-type waxes. U.S. Pat. No. 3,125,453 to Simmonds employs a mixture of triethanolamine and an acid to emulsify a mixture of waxes also for paste-type polishes.

U.S. Pat. No. 4,035,514 to Davis, teaches a water-dispersable petrolatum composition containing cetyl alcohol, lanolin alcohols and alkoxylate fatty acid esters of sorbitol.

Most of the above teach production of temporary coatings such as floor waxes, cosmetics and the like. In contrast, the present invention, possibly through the use of co-solvents which tend to form azeotropes which enhance water removal during curing, provides coatings having substantial life even in corrosive environments. While not wishing to be bound to any theory or mechanism, it appears the co-solvents tend to act as dispersing agents and additionally enhance stability of the liquid compositions at low temperatures.

Also, the inclusion of the salts of organic acids in the present invention tend to build longer-chain molecules which additionally deter corrosion and promote stability.

The coatings of the present invention find additional utility as lubricants, e.g. particularly for wire drawing and other metal drawing, extrusion and impact forming operations.

In brief review, other prior U.S. patents of interest include:

U.S. Pat. No. 3,539,367 to Yaroshevich, relating to cationic emulsions (the compositions of the present invention are not cationic emulsions);

U.S. Pat. No. 3,660,128 to Sheldahl, relating to inverted wax emulsion pastes for artwork;

U.S. Pat. No. 2,349,326 to Wilson and U.S. Pat. No. 3,125,453 to Simonds, both relating to paste type polishes;

U.S. Pat. No. 2,862,825 to Westlund et al, U.S. Pat. No. 2,943,945 to Saywell, and U.S. Pat. No. 3,565,843 to Kassinger, all relating to soluble oils, not to firm wax coatings;

U.S. Pat. No. 3,434,851 to Miller, relating to solvent-borne asphalt coatings;

U.S. Pat. No. 3,446,764 to Phillips, U.S. Pat. No. 3,699,065 to Clark, U.S. Pat. No. 4,184,991 to Scheurman III, U.S. Pat. No. 3,223,666 to Botton, U.S. Pat. No. 3,379,548 to Jen, U.S. Pat. No. 4,039,495 to Hunsucker, U.S. Pat. No. 4,051,089 to Tobias, and U.S. Pat. No. 4,081,411 to Hunsucker, all relating to base resin formulas not to completed coatings;

U.S. Pat. No. 3,494,882 to Andrews, relating to high gloss emulsified polyester emulsions;

U.S. Pat. No. 4,187,204 to Howard, relating to water-borne paint containing not over 10% water;

U.S. Pat. No. 4,225,477 to Vosishth and Wang, relating to co-solvent changes in water-borne coatings to control re-coatability (the coating's ability to form a substrate for a topcoat);

U.S. Pat. No. 4,148,948 to Williams, relating to a leveling additive for water dispersible paints; and,

U.S. Pat. No. 3,413,227 to Howard and Randell, relating to substituted benzotriazole.

Other patents considered in preparing this application are U.S. Pat. Nos.:

3,879,335, Storck, et al

2,695,910, Asseff, P. A., et al

3,565,678, Johnson, et al

4,239,648, Marshall, et al

4,059,452, Nishijima, et al

3,653,931, Burchart, et al

3,985,584, Chan, et al

4,048,374, Kotzach, et al

3,839,051, Carreny, L.

3,903,346, Delcon, et al

3,864,322, Yalloorakis, M. D.

4,062,821, Hung, T. M.

3,773,550, Tomalia, D. A.

4,036,514, Davis, R. I.

4,162,920, Gillich, T. N.

3,661,796, Erby, et al

3,313,635, Wollak, et al

3,080,221, Fessler, et al

3,738,851, Jarvis, W. H.

3,726,807, Johnson, K. L.

3,642,653, Northan et al.

Problems with metal preservative coatings, especially those primarily intended for long-term storage protection, have always existed. Prominent difficulties have been tackiness, sensitivity to water, objectionable odor, non-availability of light colored coatings and, where water-borne compositions are involved, limited high-temperature storage stability of the compositions themselves.

Many attempts have been made to modify wax emulsion type coatings to reduce their water sensitivity (fogging, clouding, stripping in the presence of water) problems without achieving the results of the present invention. Fatty emulsions, abetic acid and similar acid soaps have been utilized in temporary coatings with some degree of success, but result in coatings of poor corrosion performance and, additionally, after many months, hardening may occur causing localized corrosion of the article to be preserved.

The coating compositions of the present invention are water-borne, storage stable, even at higher temperatures, and provide coatings which usually are firm which can be light in color, which have low odor levels and which display enhanced corrosion prevention.

SUMMARY

(1) General Statement of the Invention:

The present invention relates to water-borne coating compositions of high temperature (e.g. 52° C.) storage stability which, when applied to a substrate, usually form a firm but flexible, low odor, lubricating, corrosion preventative film capable of being formulated in light colors.

More particularly, the coating compositions of the present invention, which are capable of application and flow onto a solid substrate, and comprise: (1) usually one or more waxes, (2) one or more organic esters, (3) one or more surfactants, (4) one or more coupling agents many of which are carefully selected to result in final dispersion stable at higher temperatures and (5) water; to form a water-borne dispersion for greatly improved corrosion resistance, especially when employed as a long-term metal preservative.

(2) Utility of the Invention:

The invention provides valuable coating formulations having excellent corrosion protection and storage stability.

DESCRIPTION OF THE PREFERRED EMBODIMENTS STARTING MATERIALS Waxes

Preferably the compositions of the present invention will include semirefined paraffin wax having a melting point above about 60° C., preferably above 70° C.; which contains about 0 to about 15 and more preferably 0 to about 10 weight percent oil based on the weight of the paraffin wax though other types of wax may occasionally be substituted for specialized applications. The wax can contain at least 50% by weight of essentially saturated wax such as crystalline parraffinic wax or microcrystalline wax. General paraffin waxes can be naturally derived, e.g. those manufactured in the processing of petroleum crude oils, or synthetically manufactured, e.g. polyolefin waxes such as polyethylene or polypropylene waxes. The average molecular weight of the waxes useful in the present invention should be selected so as to provide a firm film, but molecular weight is not narrowly critical and will be easily selected by those skilled in the art. Also, the degree of branching in the wax molecules should be selected so the average degree of crystallinity permits the wax to be easily dispersed and to be compatible with the other ingredients of the particular formulation being produced. Chain branching provides sites for esterification in the case of oxygenated waxes; these are also suitable for use in most applications with the present invention. Oxygenated waxes (oxwax) will preferably have an acid number in the range of from about 15 to about 200, most preferably from 25 to about 45.

The wax composition can contain 0 to 10, more preferably 0 to 8 and most preferably 0 to 5% of a hydrocarbon oil, preferably saturated (% Oil is based on the weight of the wax, but other percents are based on the total formulation weight). The oil should preferably boil above about 200° C. more preferably 175° C. and most preferably 160° C. Specific waxes useful for the present invention include: natural waxes, such as slack wax, a semirefined paraffin available from Penreco Co. of Butler, Pa.; petrolatum, widely available; synthetic waxes, such as polyethylene waxes available from Bareco Corporation of Tulsa, Okla., or the Epolene brand available from Eastman Kodak of Rochester, N.Y., or oxygenated waxes, such as oxidized petrolatum which can be readily manufactured in petroleum refineries utilizing well-known techniques. Also useful are those available from Durachem Corporation of Harrison, N.Y. Others include: Polywax 655 (Bareco), Mobil Microwax 2305 (Mobil Oil) and Shellwax, eg., Shellwax 400 and its Latin American equivalent Shellwax 300.

The amount of waxes to be utilized with the present invention is not narrowly critical and, in fact, for special applications the wax can even be omitted with additional quantities of the esters described below being employed. For most formulations the wax content will be from 0.5 to 35%, more preferably from about 5 to 30% and most preferably from about 12 to about 25% by weight.

All percents given herein are percents by weight based on the weight of the total formulation unless otherwise expressly stated.

POLYOL ESTERS

The esters useful for the present invention are preferably polyfunctional esters of carboxylic acids, preferably of fatty acids having 6 to 30 carbons. Mono-esters may find occasional use in special circumstances. Particularly preferred are the polyesters of naturally-derived fatty acids such as organic acid esters of glycerine, coconut oil, tall oil, soya oil acids, stearic acid, preferably, isostearic acid, oleic acid, linoleic acid and polyols, e.g. neopentylglycol, trimethylol propane and pentaerythrol. Most preferred is the dilanolinic acid ester of pentaerythritol.

Useful commercial polyol esters comprise: "Pentalan" from Croda Chemical Company of England, a tetrahydric lanolin alcohol; Degras manufactured by Emory Industries of Linden, N.J., and FAI manufactured by Azirona Chemical of New York City.

Table I illustrates the starting materials for a number of suitable esters.

In all four cases the PE used was in a 1:4 molar ratio to the fatty acid content of the charge and the water collected is essentially equivalent to theory on the basis of PE weight. (A slightly greater amount of water was obtained where oxwax is involved).

Ester I

75% 100 Oxwax 91

25% Lanolin FA-147

Ester II

50% Oxwax 91

50% Lanolin FA-147

PE-III

100% 100 Oxwax 91 (oxygenated wax of 91 acid number)

Ester IV

100% Lanolin FA-147 (Emory, lanolin wool grease)

Esters II and II have small amounts of insoluble resins--these were filtered out.

Adjustment of residual acid number for esters up to 25 is made with oxwax.

                                      TABLE I                                      __________________________________________________________________________     GLYCEROL AND PENTAERYTHRITOL ESTERS OF 100 NEUTRAL                             OXYGENATED WAX (93 ACID NO.)                                                   Charge (g): GE-I                                                                               GE-II                                                                              GE-III                                                                             PE-I                                                                               PE-II                                                                              PE-III                                                                             PE-IV                                      __________________________________________________________________________     Toluene     200.1                                                                              200.0                                                                              200.1                                                                              200.4                                                                              200.4                                                                              200.1                                                                              200.2                                      100 Oxwax 91                                                                               150.1                                                                              100.0                                                                              200.1                                                                              150.3                                                                              100.2                                                                              200.1                                                                              00                                         Lanolin FA 147                                                                             50.0                                                                               100.0                                                                              00  50.1                                                                               100.2                                                                              00  20.2                                       Glycerol    10.0                                                                               20.0                                                                               31.5                                                                               00  00  00  00                                         Pentaerithritol                                                                            00  00  00  11.0                                                                               22.0                                                                               33.0                                                                               44.0                                       para-Toluene Sulfonic                                                                      1.0 2.0 3.1 1.0 2.0 3.0 3.9                                        Acid-Catalyst                                                                  Total       411.2                                                                              422.0                                                                              434.8                                                                              412.8                                                                              424.7                                                                              436.1                                                                              448.3                                      H.sub.2 o/Azeotrope (g)                                                                    6.0+                                                                               9.5+                                                                               12.0                                                                               5.5 8.0 12.7                                                                               13.2                                       Toluene-320°                                                                        *-- *-- 161.1                                                                              163.7                                                                              174.3                                                                              166.6                                                                              171.0                                      Product     233.7                                                                              238.8                                                                              259.6                                                                              240.2                                                                              243.5                                                                              251.6                                                                              254.7                                      Residues    0.4 1.3 2.2 0   61  5.4 10.0                                       Total       --  --  434.9                                                                              409.4                                                                              425.8                                                                              436.3                                                                              448.9                                      Product                                                                        Acid No.    33.4                                                                               14.6                                                                               9.2 26.8                                                                               12.5                                                                               22.1                                                                               12.3                                       Saponification No.                                                                         197 170 150 174 167 202 174                                        Wt. % Yield 56.8                                                                               56.5                                                                               59.7                                                                               58.2                                                                               57.3                                                                               57.1                                                                               56.8                                       Wt. % Toluene in Prod.                                                                     --  --  15.0                                                                               15.1                                                                               10.7                                                                               13.3                                                                               11.5                                       __________________________________________________________________________      *Lost condenser water                                                    

The quantity of esters employed with the present invention will not be narrowly critical and will depend to a substantial degree on the other ingredients and their amounts as selected for the particular formulation. Preferably the compositions will contain from about 5% to about 30%, more preferably from about 5% to about 10% and most preferably from about 8% to about 12% percent esters based on the total weight of the esters as compared to the total weight of the formulation.

SURFACTANTS

Surfactants useful with the present invention include natural surfactants such as salts of oleic acid, e.g. morpholine salts of oleic acid, or the similar salt of triethanolamine and entirely synthetic surfactants such as alkanol amide, e.g. WHC by Stepan Chemical Company of Chicago, Ill. (oleyl diethanol amide), sorbitan monooleates manufactured by ICI America of Wilmington, Del., isostearic acid salts, coconut oil salts, lauric acid salts and the like. Excess carboxylic acid, e.g. in the wax components, can react with amines in situ to form salts which act as surfactants. The preferred range is 2 to 8% carboxylic acid and 1 to 5% amine. All or part of the surfactant can be organic sulfonates, e.g. alkyl lauryl sulfonate or alkyl benzene sulfonates.

Suitable surfactants comprise the reaction products of amines such as morpholine, triethanolamine, ammonia, diethanolamine and ethanolamine with carboxylic acids such as those mentioned above. The compositions of the present invention will generally include surfactants in the amount of from about 0.5 to about 12, more preferably from about 2 to about 8 and most preferably from about 3 to about 7 percent by weight based on the weight of the formulation. However, this will vary in response to the selection and quantities of the other ingredients employed.

COUPLING AGENTS

The use of coupling agents is a special feature of the invention. Preferred coupling agents comprise C₅ -C₃₀ liquid hydrocarbon coupling component and C₂ -C₂₀ alcohol in a weight ratio of between 1:1 and 10:1, respectively.

Several types of coupling agents can be employed with the invention including mineral spirits, e.g. ethylene glycol ethers, preferably butyl and propyl ethers; hydroxy ethers (ether-alcohols), such as propyl cellosolve, (Ektasolve EP manufactured by Eastman Kodak of Rochester, N.Y.), diethylene glycol monoethyl ether, monopropyl ether, of ethylene glycol, propyl cellosolve, ethyl cellosolve, and diethylene glycol monoethyl ether, and other coupling agents which will be evident to those skilled in the art for use in specialized formulations according to the present invention. The coupling agent is selected by physical test; subsutituted alcohols or hydrocarbons and anything which does not interfere with the formulations of the present invention and which renders their ingredients mutually soluble in the water base will will generally be acceptable.

Alcohol ether-esters may also be used e.g. ethylene glycol monoacetate, diethylene glycol monoproprionate, diethylene glycol monoacetate, and propylene glycol monoacetate.

Alcohols, such as ethanol, isopropanol and isobutanol will generally be useful as coupling agents for the invention. Other commercial coupling agents which are useful with formulations of the present invention include: Ektasolve EP, manufactured by Eastman Kodak of New York, and Propasol P, manufactured by Union Carbide of Danbury, Conn.

The coupling agents of the present invention will generally be employed in quantities of from about 1% to about 20% or more, more preferably from about 3 to about 18%, and most preferably from about 4 to about 15% based on the weight of the formulation. In addition to acting as a coupling compound, the coupling agent will usually be useful during the drying and curing process after application of the coatings composition of the present invention to substrates. For example, when carefully selected, the coupling agent will form an azeotrope with the water present in the formulation, thus increasing volatility, speeding cure, and providing a more permanent coating. Some coupling agents will assist the final coating in other ways, e.g. by providing leveling of the final coating, avoiding pinholes and providing a more continuous, better quality dry film.

WATER

Deionized water will preferably be employed with the formulations of the present invention in order to prevent reaction of chlorine, calcium, magnesium or other components of tap water from interfering with the formulations or their curing. Distilled water could, of course, be employed but will generally be avoided for economic reasons.

Formulations of the present invention will generally contain a minimum of about 35%, more preferably 45% and most preferably 60% or even more of water based on the total weight of the formulation. As the formulations of the present invention are generally classifiable as oil-in-water emulsions of special character, a quantity of water greater than about 92% may cause swelling and loss of wetting properties in most of the formulations of the present invention although specialized formulations utilizing carefully selected non-aqueous ingredients may tolerate water up to an amount of 97% by weight based on the weight of the total formulation.

pH

The pH of this system will be preferably in the range of 7.0-10 with 8.0-9.0 being preferred. The nature of the emulsion will depend heavily upon the amount of soap produced when the emulsifying agent (fatty acid) is neutralized with an alkaline material (e.g. amines, triethanolamine, morpholine). One should slightly overbase (make alkaline) the system to obtain maximum soap production by reacting any residual acids which may be left over at the normal end point of titration. Excessive amounts of base will form an extremely "hard" salt which is not miscible in water, thus causing the aqueous and non aqueous phases to separate.

HLB

Hydrophile-lipophile balance--In the selection of amides for this system one should obtain an amide with an HLB value of about 8 to 12, preferably 9 to 11 to facilitate making an oil in water emulsion. An anionic surfactant would be preferred due to its better corrosion inhibiting properties.

TECHNIQUES IN MIXING

Apparatus: The apparatus for the present invention will be that conventionally utilized in the preparation of coatings compositions, e.g. kettles and mixing tanks having flow metering or measuring devices and agitation means, e.g. pumps mounted on side-arms connecting with the main vessel, internal stirrers, contra-rotating shearing devices and any of the other available devices which are well known to the art.

Temperature: The temperature during mixing may be different during different stages in the formulation. In general the water will be at about 200° F. (93° C.), the non-aqueous ingredients will be transferred and mixed together at about 225° F. (107° C.). However, these temperatures are not narrowly critical and will vary to provide faster mixing or better compatibility of ingredients according to observation of those skilled in the art. For example, pressure vessels may be utilized for the purpose of lowering ingredient melting and boiling points, where useful, in order to provide better dispersion of difficult-to-mix ingredients.

Mixing Procedure: While the formulations of the present invention may be manufactured continuously if desired, batch techniques will be more usually employed. For example, the total amount of water desired in the finished formulation (e.g. 1700 gallons, 6,562 liters) is heated in a mixing vessel large enough to hold the entire batch of formulation until the water temperature is approximately 195° F. (90° C.). The wax, if any, esters, surfactants, coupling agents and any other non-aqueous ingredients are heated in a separate vessel until the temperature reaches about 225° F. (107° C.) with the various non-aqueous ingredients being added slowly while the vessel is agitated with conventional mixer. In most cases, the esters will be added with the carboxylic acids; the neutralizing ingredient, e.g. morpholine, triethanolamine, will be added after the other ingredients have been thoroughly mixed. After neutralization, which is generally visually observable as a distinct increase in viscosity, the non-aqueous ingredients are allowed to mix for 15 to 30 minutes and transferred over to the aqueous phase, which is agitated during the addition of the non-aqueous phase. Heating is discontinued after addition of the non-aqueous phase, and the finished formulation is allowed to cool with, preferably, constant agitation, after which the formulation is drawn off into shipping containers, e.g. tank cars, tank trucks, drums or smaller cans.

QUALITY CONTROL

The finished formulation, prior to packaging, will generally be checked for pH, solids content, freeze-thaw stability, corrosion-protection under accelerated conditions and other tests utilizing techniques well known to the coatings industry.

APPLICATION

The formulations of the present invention may be applied to substrates to be protected by conventional application techniques, such as spraying, brushing, roller-coating, dipping, flow-coating, electrostatic airless spraying. Coating thickness can be varied by changing the formulation, the number of coats, or the amount applied per coat but in general will be in the range from about 0.5 to about 3 mils per coat after drying.

EXAMPLES EXAMPLE I

(Formulation according to the invention providing long term protection)

Forty-six and one half parts by weight of deionized water are charged to a conventional mixing kettle rotary agitator and brought to a boil. Twenty parts of 400 Shellwax, ten parts of pentaerythritol dilanolate, six parts of oleic acid, ten parts of 140 flash mineral spirits, and five parts Ektasolve EP are charged to a second vessel also having a stirred reactor which is heated to 225° F. (107° C.) with agitation. Two parts of morpholine and one half part of triethanolamine are then added to the organic phase and heat is terminated, after a few minutes, a thickening is observed, indicating the neutralization reaction has proceeded. The heating is stopped, and the contents of the non-aqueous vessel are immediately transferred to the vessel containing the water with continuous stirring. Heating is then terminated and the mixture continuously agitated until it cools into 100° F. (38° C.). The pH is then adjusted to 8.5 by addition of less than one part of morpholine. About three parts of water are added to compensate for water lost during heating. The solids content is then found to be about 35%.

The resulting product is tested for corrosion resistance by applying to a cold rolled 1010 steel panel. After drying for 72 hours the test panel is subjected to a 5% salt (NaCl) spray at a temperature of 95° F. (35° C.) according to ASTM test B-117. The test panel resists failure (corrosion) for 700 hours.

A similar test panel coated with the formulation of this example I resists 2,000 hours of exposure to 100% relative humidity at 120° F. (44° C.) according to the techniques of ASTM D-1748.

A sample of the above formulation survives five successive freeze-thaw cycles each comprising 16 hours at 0° F. (-18° C.) followed by eight hours at 77° F. (25° C.) with no separation or other evident deleterious effect.

A sample of the above formulation withstands 144 hours at 120° F. (49° C.) without separation or other observable deleterious effect.

When a panel as previously described is dipped into the above formulation and allowed to dry at room temperature and approximately 50% relative humidity, the coating is cured and dry to the touch in 60 minutes.

The thickness on the above test panels is approximately 2 mil (approximately 48 microns).

EXAMPLES II-VIII

When various formulations are produced according to the parameters set forth in Table II, the results are as described in Table II and as set forth below:

EXAMPLE II

This is a formulation produced according to the techniques of Example I and is similar to it, except that 25% of 300 Shellwax is used in place of 20% 400 Shellwax, Rule 66 mineral spirits are used instead of 140 solvent, about 40% water is used instead of about 46%, and 1% triethanolamine is used instead of 0.5%. High temperature emulsibility, viscosity, and film characteristics are essentially equivalent to those of Example I.

EXAMPLE III

This is a formulation produced according to the techniques of Example I and is similar to it, except that 35% of 400 Shellwax is used instead of 25%, Ektasolve EP is absent, 5% oleic acid is used instead of 6%, and about 38% water is used instead of about 46%. High temperature emulsibility is inferior to Example I, but acceptable. Viscosity is moderately higher than that for Example I, probably because of lower water and oxygenated cosolvent content. Film properties are adequate for processing.

EXAMPLE IV

This is a formulation produced according to the techniques of Example II and is similar to it, except that 8% Ektasolve EP is used instead of 5% and about 38% water is used instead of about 40%. Viscosity is significantly higher than that of Example III and far higher than that of Example II, probably because of a much higher level of oxygenated solvent.

EXAMPLE V

This is a formulation produced according to the techniques of Example I and is similar to it, except that 35% of 400 Shellwax is used instead of 20%, 5% dipentaerythritol is used instead of 10%, 10% Ektasolve EP is used instead of 5%. 140 solvent is absent, morpholine is absent, 2% triethanolamine is used instead of 0.5%, 5% oleic acid is used instead of 6%, and about 43% water is used instead of about 46%. The emulsion is poor and also fails at high temperature, probably because of the absence of hydrocarbon solvents.

EXAMPLE VI

This is a formulation produced according to the techniques of Example II and is similar to it, except that 25% 300 Shellwax is used instead of 20%, Ektasolve EP is absent, 2% triethanolamine is used instead of 1%, and 4% oleic acid is used instead of 6%. The emulsion is poor and also fails at high temperature, probably because of the absence of oxygenated solvent.

EXAMPLE VII

This is a formulation produced according to the techniques of Example II, and is similar to it, except that 25% oxygenated petrolatum (acid no. 45) is used instead of 20%, 300 Shellwax and 2.5% Ektasolve EP is used instead of 5%. The film is somewhat softer than that of Example II, probably because the base vehicle, oxygenated petrolatum, is softer than the base vehicle, 300 Shell Microwax, of Example II. The emulsion is poor and also fails at high temperature, possibly because of the lower melting point of the oxygenated petrolatum used in Example VII.

EXAMPLE VIII

This is a formulation produced according to the techniques of Example II and is similar to it, except that 20% of low oil (1/2% oil) slack wax is used instead of 20% 400 Shellwax, Rule 66 mineral spirits is absent, 10% Ektasolve EP is used instead of 5%, 3% oleic acid is used instead of 6%, and about 55% water is used instead of about 46%. The emulsion breaks upon standing at room temperature. More oleic acid is then added (2%) in order to improve the surfactant. The emulsion resulting is stable but fails high temperature testing after two weeks. The drying time is somewhat slow (3 hrs.). Both effects may be due to the absence of hydrocarbon solvent.

                                      TABLE II                                     __________________________________________________________________________     EXAMPLE:     I  II    III  IV    V    VI    VII  VIII                          __________________________________________________________________________     RUN NUMBER:  2-78                                                                              2-65  2-68 2-75  2-59 2-67  2-66 2-54                          400 Shellwax 20       35         35                                            300 Shellwax    25         25         25                                       Oxidized Petrolatum*                        25                                 330 Slack Wax (1/2% Oil)                         20                            Pentaerythritol Dilanolate                                                                  10 10    10   10    5    10    10   10                            Rule 66 Min. Spirits                                                                        -- 10    10   10    --   10    10   --                            Ektasolve EP 5  5     --   8     10   --    2.5  10                            140 Flash Solvent                                                                           10 --    --   --    --   --    --   --                            Water        46.5                                                                              41    37.5 38    43   47    46   55                            Morpholine   2  2     2    2     --   2     2    2                             Triethanolamine                                                                              0.5                                                                              1      0.5 1     2    2     1    1                             Oleic Acid   6  6     5    6     5    4     6    3(+2)                         Test Results                                                                   Emulsion Stability                                                                          pass                                                                              pass  pass pass  fail pass  pass pass                          Storage Stability                                                                           pass                                                                              pass  fair pass  fail fail  fail fail                          Freeze-Thaw  pass                                                                              pass  pass pass  pass pass  pass pass                          Viscosity    good                                                                              good  viscous                                                                             extremely                                                                            viscous                                                                             viscous                                                                              good viscous                                                  viscous                                             Film Integrity                                                                              Firm                                                                              Firm  Firm Firm  Firm Firm  Soft Firm                          Drytime (Minutes)                                                                           70 70    100  100   180  120   120  180                           Early H.sub.2 O Resistance                                                                  good                                                                              good  good good  poor fair  poor fair                          Salt Spray (ASTM B117):                                                        Cold Rolled Steel (Bare)                                                                    400                                                                               400   400  400        400   400  --                            Carbon Steel (Polished)                                                                     700                                                                               700   580  700   400  700   --   --                            Thickness (mil)                                                                             2  2     2    2     2    2     2    2                             Humidity ASTM D-1748                                                                        2000                                                                              2000  2000 2000  2000 2000  --   2000                          Sprayability good                                                                              good  good good  poor poor  --   --                            Comments     best                                                                              no    viscous                                                                             extremely                                                                            viscous                                                                             low in                                                                               poor poor                                       made                                                                              change                                                                               not  viscous                                                                              wax  emulsifier                                                                           emulsion                                                                            drying                                        in    enough                                                                              cosolvent                                                                            not  and   stability                                                                           and                                           properties                                                                           water                                                                               ratio properly                                                                            oxygenated stability                                           for  wrong dispersed                                                                           solvent    needs                                               dilution                   aliphatic                                                                      solvent                       __________________________________________________________________________      *Acid no. of about 50                                                    

MODIFICATIONS

It will be understood by those skilled in the art that the invention is not to be restricted by the examples which merely illustrate the invention and that the invention is susceptible to a wide variety of modifications and variations without departing from the spirit thereof. For example, the formulations of the invention can be prepared as concentrates to which a substantial amount of water can be added in order to avoid shipping of water, particularly for international or other long distance shipment. The formulations may contain other useful ingredients such as biocides, antifoam agents, pigments, dyes and leveling agents, well known to those skilled in coatings technology. 

What is claimed is:
 1. An anti-corrosive, storage stable, rapidly drying, emulsified oil in water and water reducible and dispersible coating composition, capable of application and flow on a solid substrate, comprising:(a) about 0.5 to 35% by weight of organic wax components containing less than about 10% oil based on the weight of the wax and having a melting point above 70° C.; (b) about 5 to 30% of a polyol ester derived from the polyester of one of:stearic acid, isostearic acid, oleic acid, linoleic acid and lanolinic acid, and a polyol selected from the group consisting of:neopentyl glycol, trimethylol propane, pentaerythritol and dipentaerythritol; (c) about 0.5 to 12% of surfactant; (d) about 1 to 20% of a coupling agent comprising a C₅ -C₃₀ liquid hydrocarbon coupling component and a C₂ -C₂₀ alcohol in a ratio of between 1:1 and 10:1 respectively, and wherein said coupling agent is at least one of mineral spirits, ether alcohols and alcohol ether-esters selected from the group consisting of:mineral spirits, ethylene glycol ether, propyl cellosolve, diethylene glycol monoethyl ether, ethylene glycol monopropyl ether, butyl cellosolve, ethyl cellosolve, ethylene glycol monoacetate, diethylene glycol monoproprionate, diethylene glycol monoacetate, propylene glycol monoacetate, ethanol, isopropanol and isobutanol; (e) about 35 to 97% of water;said percents being based on the weight of the total formulation except as noted.
 2. A composition of claim 1, in which said coating further comprises about 2 to 8% of a carboxylic acid, and about 1 to 5% of an amine, said acid and said amine forming a salt providing at least a portion of of said surfactant.
 3. A composition of claim 2, in which said coating further comprises an emulsifiable amide or an organic sulfonate replacing part of said carboxylic acid and said amine.
 4. A composition of claim 1, in which said wax is admixed with up to 15% of hydrocarbon oil as based on the weight of the wax components.
 5. A composition of claim 4, in which said hydrocarbon oil is an essentially saturated oil boiling above 175° F.
 6. A composition of claim 1, which contains at least 50%, by weight, of essentially saturated wax.
 7. A composition of claim 6, in which all or part of said essentially saturated wax is crystalline paraffinic wax.
 8. A composition of claim 7, in which said crystalline paraffinic wax comprises one or more of the following: slack wax, petrolatum and micro-crystalline wax.
 9. A composition of claim 2, in which said amine is chosen from a group of the following: morpholine, triethanolamine, ammonia, diethanolamine, ethanolamine.
 10. A composition of claim 2, in which said coating further comprises oleyl diethanol or sorbitan mono oleate.
 11. A composition of claim 1, in which said coupling agent comprises an ether-alcohol.
 12. A composition of claim 11, in which said ether-alcohol is chosen from a group of the following: propyl cellosolve, butyl cellosolve, ethyl cellosolve, diethylene glycol monoethyl ether.
 13. A composition of claim 1, in which said coupling agent is an alcohol ether-ester.
 14. A composition of claim 13, in which alcohol ether-ester coupling agent is chosen from a group of the following: ethylene glycol monoacetate, diethylene glycol monoproprionate, diethylene glycol monoacetate and propylene glycol monoacetate.
 15. A method of producing an anti-corrosive, storage stable, rapidly drying, emulsified oil in water and water reducible and dispersible coating composition, capable of application and flow on a solid substrate, comprising the following steps:(a) mixing, in an essentially fluid state:a wax component, a polyol ester derived from the polyester of one of:stearic acid, isostearic acid, oleic acid, linoleic acid and lanolinic acid, and a polyol from the group consisting of:neopentyl glycol, trimethylol propane, pentaerythritol and dipentaerythritol; carboxylic acid, and a coupling agent comprising a C₅ -C₃₀ liquid hydrocarbon coupling component and a C₂ -C₂₀ alcohol in a ratio of between 1:1 and 10:1 respectively, and wherein said coupling agent is at least one of mineral spirits, ether alcohols and alcohol ether-esters elected from the group consisting of:mineral spirits, ethylene glycol ether, propyl cellosolve, diethylene glycol monoethyl ether, ethylene glycol monopropyl ether, butyl cellosolve, ethyl cellosolve, ethylene glycol monoacetate, diethylene glycol monopropionate, diethylene glycol monoacetate, propylene glycol monoacetate, ethanol, isopropanol and isobutanol; (b) neutralizing to a pH of about 7 to 11, with an amine; (c) adding water, with agitation, at such temperature so as to cause dispersion of the mixture; and (d) adjusting the pH of the total mixture from about 7 to about
 11. 16. The method of producing a coating composition of claim 15, capable of high temperature, long term storage, wherein said coupling agent comprises propyl cellosolve.
 17. A method of claim 15, in which part of said carboxylic acid and amine are replaced by an emulsifiable amide or an organic sulfonate.
 18. A method for coating solid substrates, wherein said composition of claim 1 is applied to metal.
 19. A method for coating solid substrates, wherein said composition of claim 1 is applied by dipping.
 20. A method for coating solid substrates, wherein said composition of claims 1 is applied by brushing.
 21. A method for coating solid substrates, wherein said composition of claims 1 is applied by rolling.
 22. A method for coating solid substrates, wherein said composition of claims 1 is applied by electrostatic spraying.
 23. A method for coating solid substrates, wherein said composition of claims 1 is applied by hand spraying.
 24. A composition of claim 2 in which at least a portion of said carboxylic acid is contained in said wax components.
 25. A manufacture comprising a substrate coated with a coating composition of claim
 1. 26. A composition according to claim 1 comprising:(a) about 5 to 30% of composition (a); (b) about 5 to 10% of component (b); (c) about 2 to 8% of component (c); (d) about 3 to 18% of component (d); and (e) about 45 to 97% of component (e).
 27. A composition according to claim 1 comprising:(a) about 12 to 25% of component (a); (b) about 8 to 12% of component (b); (c) about 3 to 7% of component (c); (d) about 4 to 15% of component (d); and (e) about 60 to 97% of component (e).
 28. An emulsified oil in water reducible and dispersible coating composition, capable of application and flow on a solid substrate, comprising:(a) 20% wax; (b) 10% pentaerythritol dilanolate; (c) 6% oleic acid; (d) 10% mineral spirits; (e) 6% propyl cellosolve; (f) 2% morpholine; (g) 1% triethanolamine; and (h) 46.5% water.
 29. The composition of claim 4 admixed with up to 10%, more preferably up to 8%, and most preferably up to 5% of hydrocarbon oil.
 30. A composition of claim 1, wherein said organic wax components comprises oxygenated waxes having an acid number in the range of from 15 to about 200, and most preferably from 25 to about
 45. 31. A composition of claim 1, wherein the pH is in the range of 7.0 to 10, and preferably 8.0 to 9.0.
 32. An anti-corrosive, storage stable, rapidly drying, emulsified oil in water and water reducible and dispersible coating composition, capable of application and flow on a substrate comprising:(a) about 0.5 to 35% by weight of organic wax components containing less than about 10% oil based on the weight of the wax and having a melting point above 70° C.: (b) about 5 to 30% of polyol ester derived from the polyester of one of:stearic acid, isostearic acid, oleic acid and lanolinic acid, and a polyol selected from the group consisting of:neopentyl glycol, trimethylol propane, pentaerythritol and dipentaerythritol; (c) about 2 to 8% carboxylic acid; (d) about 1 to 20% of a coupling agent comprising a C₅ -C₃₀ liquid hydrocarbon coupling component and a C₂ -C₂₀ alcohol in a ratio of between 1:1 and 10:1 respectively, and wherein said coupling agent is at least one of mineral spirits, ether alcohols and alcohol ether-esters selected from the group consisting of:mineral spirits, ethylene glycol ether, propyl cellosolve, diethylene glycol monoethyl ether, ethylene glycol monopropyl ether, butyl cellosolve, ethyl cellosolve, ethylene glycol monoacetate, diethylene glycol monoproprionate, diethylene glycol monoacetate, propylene glycol monoacetate, ethanol, isopropanol and isobutanol; (e) about 1 to 5% amine; and (f) about 35 to 97% water.
 33. A method according to claim 15, wherein step (a) is conducted at about 107° C., the water at step (c) is boiling water, and step (d) is performed after the mixture has cooled to about 38° C.
 34. A method of producing an emulsified oil in water and water reducible and dispersible coating composition, capable of application and flow on a solid substrate, comprising the followin steps:(a) mixing in an essentially fluid state, 20% wax, 10% pentaerythritol dilanolate, 6% oleic acid, 10% mineral spirits, and 6% propyl cellosolve; (b) adding 2% morpholine and 1% triethanolamine with further mixing; (c) adding 46.5% water with agitation, at such temperatures so as to cause dispersion of the mixture; and (d) adding less than 1% morpholine to adjust the pH to 8.5
 35. A composition of claim 1, in which the polyol ester is pentaerythritol dilanolate. 